Browsing by Author "Popovici, N."
Now showing 1 - 4 of 4
Results Per Page
Sort Options
- KrF pulsed laser deposition of chromium oxide thin films from Cr8O21 targetsPublication . Popovici, N.; Parames, M. L.; Da Silva, R. C.; Monnereau, O.; Sousa, P. M.; Silvestre, António Jorge; Conde, O.Chromium oxides, CrxOy, are of great interest due to the wide variety of their technological applications. Among them, CrO2 has been extensively investigated in recent years because it is an attractive compound for use in spintronic heterostructures. However, its synthesis at low temperatures has been a difficult task due to the metastable nature of this oxide. This is indeed essential to ensure interface quality and the ability to coat thermal-sensitive materials such as those envisaged in spintronic devices. Pulsed Laser Deposition (PLD) is a technique that has the potential to meet the requirements stated above. In this work, we describe our efforts to grow chromium oxide thin films by PLD from Cr8O21 targets, using a KrF excimer laser. The as-deposited films were investigated by X-ray diffraction and Rutherford backscattering spectrometry. Structural and chemical composition studies showed that the films consist of a mixture of amorphous chromium oxides exhibiting different stoichiometries depending on the processing parameters, where nanocrystals of mainly Cr2O3 are dispersed. The analyses do not exclude the possibility of co-deposition of Cr2O3 and a low fraction of CrO2.
- KrP laser CVD of chromium oxide by photodissociation of Cr(CO)(6)Publication . Sousa, P. M.; Silvestre, António Jorge; Popovici, N.; Parames, M. L.; Conde, O.This work reports on the synthesis of chromium oxide thin films prepared by photodissociation of Cr(CO)(6) in an oxidizing atmosphere, using a pulsed UV laser (KrF, lambda = 248 nm). The experimental conditions, which should enable the synthesis of CrO2, are discussed and results on the deposition of CrxOy films on Al2O3 (0001) substrates are presented.
- Morphological and structural characterization of CrO2/Cr2O3 films grown by laser-CVDPublication . Sousa, P. M.; Silvestre, António Jorge; Popovici, N.; Conde, O.This work reports on the synthesis of chromium (III, IV) oxides films by KrF laser-assisted CVD. Films were deposited onto sapphire substrates at room temperature by the photodissociation of Cr(CO)(6) in dynamic atmospheres containing oxygen and argon. A study of the processing parameters has shown that partial pressure ratio Of O-2 to Cr(CO)(6) and laser fluence are the prominent parameters that have to be accurately controlled in order to co-deposit both the crystalline oxide phases. Films consistent with such a two-phase system were synthesised for a laser fluence of 75 mJ cm(-2) and a partial pressure ratio of about 1. (c) 2005 Elsevier B.V. All rights reserved.
- Phase growth control in low temperature PLD Co: TiO2 films by pressurePublication . Rout, S.; Popovici, N.; Dalui, S.; Parames, M. L.; Silva, R. C. da; Silvestre, António Jorge; Conde, O.This paper reports on the structural and optical properties of Co-doped TiO2 thin films grown onto (0001)Al2O3 substrates by non-reactive pulsed laser deposition (PLD) using argon as buffer gas. It is shown that by keeping constant the substrate temperature at as low as 310 degrees C and varying only the background gas pressure between 7 Pa and 70 Pa, it is possible to grow either epitaxial rutile or pure anatase thin films, as well as films with a mixture of both polymorphs. The optical band gaps of the films are red shifted in comparison with the values usually reported for undoped TiO2, which is consistent with n-type doping of the TiO2 matrix. Such band gap red shift brings the absorption edge of the Co-doped TiO2 films into the visible region, which might favour their photocatalytic activity. Furthermore, the band gap red shift depends on the films' phase composition, increasing with the increase of the Urbach energy for increasing rutile content. (C) 2012 Elsevier B.V. All rights reserved.