Análise comparativa do desempenho das propriedades mecânicas de pastas de cimento e argamassas com adição de Óxido de Grafeno
| dc.contributor.advisor | Silva, Pedro Soares Raposeiro da | |
| dc.contributor.advisor | Evangelista, Luís Manuel Rocha | |
| dc.contributor.author | Junior, Ibraim Aragão Oliveira | |
| dc.date.accessioned | 2023-12-21T15:21:47Z | |
| dc.date.available | 2023-12-21T15:21:47Z | |
| dc.date.issued | 2022 | |
| dc.description | Trabalho final de Mestrado para obtenção do grau de Mestre em Engenharia Civil | pt_PT |
| dc.description.abstract | O óxido de grafeno (OG) é, atualmente, um dos materiais mais resistentes do mundo e possui características que levaram diversos pesquisadores a realizarem experimentos para analisar sua influência em materiais à base de cimento. Através de campanhas experimentais realizadas, foi possível perceber que a utilização deste nanomaterial gerou resultados positivos nas propriedades mecânicas dos materiais à base de cimento, porém reduziu-se sua fluidez, aumentou a viscosidade e diminuiu o tempo de presa. Por esses motivos, a utilização de aditivo superplastificante é comum nas campanhas aqui relatadas, buscando a redução desses efeitos negativos. A utilização desse nanomaterial gera nas propriedades mecânicas das pastas de cimentos e argamassas uma melhoria significativa. Na resistência à compressão chega a ter taxas de aumento de até 60% em relação à amostra de controle. E os melhores resultados da resistência à compressão estão nas adições de 0,04% a 0,06% de OG em relação à massa de cimento. Nas resistências à flexão e à tração são as propriedades que o OG gera melhores resultados e são de até 80% de taxa de aumento em relação às amostras de controle. A adição ótima para estas duas resistências mecânicas é a adição de 0,03% de OG em relação à massa de cimento. Essa diferença de resultados de acordo com a quantidade de OG inserido na mistura pode ser explicada pela formação dos cristais de hidratação do cimento. Nas adições de até 0,03% de OG, são formados cristais de hidratação com o formato de flores e que geram melhoria nas resistências à flexão e à tração. E, a partir da adição de 0,04% de OG, são formados cristais poliédricos, os quais geram melhorias na resistência à compressão. Portanto, o óxido de grafeno, além de melhorar as propriedades mecânicas dos materiais à base de cimento em até 80%, este material pode controlar a formação de cristais de hidratação e, consequentemente, as melhorias em diferentes propriedades mecânicas. | pt_PT |
| dc.description.abstract | Graphene oxide (GO) is currently one of the strongest materials in the world and has properties that have led several researchers to carry out experiments to analyze its influence on cement-based materials. Through experimental campaigns carried out, it was possible to perceive that the use of this nanomaterial generated positive results in the mechanical properties of cement-based materials, however its workability was reduced, the viscosity was increased, and the setting time was reduced. For these reasons, the use of superplasticizer additive is common in the campaigns reported in this dissertation, seeking to reduce the negative effects. The use of this nanomaterial generates a significant improvement in the mechanical properties of cement pastes and mortars. In compressive strength, it has an increase rate of up to 60% compared to the control sample. And the best results of the compressive strength are in the additions of 0.04% to 0.06% of GO in relation to the cement mass. The flexural and tensile strengths are the properties that the GO generates the best results and are up to 80% increase rate in relation to the control samples. The optimal addition for these two mechanical strengths is the addition of 0.03% GO in relation to the cement mass. This difference in results according to the amount of GO inserted in the mixture can be explained by the formation of the hydration crystals of the cement. In the additions up to 0.03% of GO, hydration crystals with the shape of flowers are formed, which improve the flexural and tensile strengths. And, from the addition of 0.04% of GO, polyhedral crystals are formed, which generate improvements in the compressive strength. Therefore, graphene oxide, in addition to improving the mechanical properties of cement-based materials by up to 80%, this material can control the formation of hydration crystals and, consequently, improvements in diferente mechanical properties. | |
| dc.description.version | N/A | pt_PT |
| dc.identifier.citation | JUNIOR, Ibraim Aragão Oliveira - Análise comparativa do desempenho das propriedades mecânicas de pastas de cimento e argamassas com adição de Óxido de Grafeno. Lisboa: Instituto Superior de Engenharia de Lisboa, 2022. Dissertação de Mestrado. | pt_PT |
| dc.identifier.tid | 203371771 | |
| dc.identifier.uri | http://hdl.handle.net/10400.21/16725 | |
| dc.language.iso | por | pt_PT |
| dc.peerreviewed | yes | pt_PT |
| dc.rights.uri | http://creativecommons.org/licenses/by-nc-nd/4.0/ | pt_PT |
| dc.subject | Óxido de grafeno | pt_PT |
| dc.subject | Argamassa | pt_PT |
| dc.subject | Pasta de cimento | pt_PT |
| dc.subject | Propriedades mecânicas | pt_PT |
| dc.subject | Graphene oxide | |
| dc.subject | Mortar | |
| dc.subject | Cemente paste | |
| dc.subject | Mechanical properties | |
| dc.title | Análise comparativa do desempenho das propriedades mecânicas de pastas de cimento e argamassas com adição de Óxido de Grafeno | pt_PT |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| oaire.citation.conferencePlace | Lisboa: Instituto Superior de Engenharia de Lisboa | pt_PT |
| rcaap.rights | openAccess | pt_PT |
| rcaap.type | masterThesis | pt_PT |