Loading...
4 results
Search Results
Now showing 1 - 4 of 4
- Formation of intermetallic structures at the interface of steel-to-aluminium explosive weldsPublication . Carvalho, Gustavo; Galvão, Ivan; Mendes, R.; Leal, Rui; Loureiro, A.The formation of intermetallic structures at the interface of carbon steel to 6082 aluminium alloy explosive welds and their influence on the weldability of these two materials were studied. The morphology, the microstructure, the chemical and phase compositions of the welds were characterised by several types of microscopy techniques. The interface characterisation proved that explosive mixtures with a lower detonation velocity were revealed as being more suitable for achieving consistent welds since jet entrapment was prevented and continuous molten layers were not formed at the weld interface. It was also found that the physical properties of the intermetallic phases generated at the weld interface have a strong influence on the weldability of steel-to-aluminium explosive welds. Specifically, it was shown that the formation of aluminium-rich intermetallic phases at the weld interface increases the solidification time of the interfacial molten material, decreasing the weldability of these two materials. The formation of these intermetallic compounds should be avoided by reducing the interaction between the flyer and the baseplate as well as by avoiding excessive molten layers.
- Effect of the flyer material on the interface phenomena in aluminium and copper explosive weldsPublication . Carvalho, Gustavo; Mendes, R.; Leal, Rui; Galvão, Ivan; Loureiro, AltinoThe effect of physical and mechanical properties of three different flyers on the interface phenomena of partially overlapped explosive welds, using the same base plate material, was studied. Flyers of Copper Cu-DHP and aluminium alloy 6082 (tempers T6 and O) were welded to AA6082-T6 base plates. The morphology of the weld interface is strongly influenced by the physical and mechanical properties of the flyer. In the interface of the aluminium welds, the use of a flyer of lower hardness and yield strength than the base plate results in asymmetrical waves, with bigger amplitude and smaller wavelength than the weld series of similar temper, and higher mechanical properties. The copper-aluminium welds presented flat interfaces, mainly because of the significant differences in melting temperature and density between the copper flyer and the aluminium base plate. Considering these results and analysing several dissimilar welds carried out by other authors it was found that when the product of density and melting temperature ratios between the flyer and the base plate exceeds a certain value, there is no formation of waves at the interface of the metals. Furthermore, for the Cu-Al welds, the CuAl2 (theta) intermetallic phase was formed on the bond zone.
- Explosive welding of aluminium to stainless steelPublication . Carvalho, Gustavo; Galvão, Ivan; Mendes, R.; Leal, Rui; Loureiro, A.Explosive welds of stainless steel and aluminium could only be achieved with the steel positioned as the baseplate. Using stainless steel as the flyer plate, the tensile stresses arrive at the interface before the complete solidification of the localised melting and no bonding is achieved. The poor weldability in this configuration is mainly related to the very low thermal conductivity of the flyer compared to the baseplate. The position of the materials significantly influences the weldability, and the ideal material for the flyer should have a higher melting temperature, specific heat and thermal conductivity, and a lower density compared to the baseplate. Some intermetallic formation is inevitable in dissimilar welds of combinations that can easily form intermetallic phases. The time-velocity diagram proved to be a reliable tool to analyse the weldability, especially when used in conjunction with the weldability window.
- Aluminum-to-steel cladding by explosive weldingPublication . Carvalho, Gustavo; Galvão, Ivan; Mendes, Ricardo; Leal, Rui; Loureiro, AltinoThe production of aluminum-carbon steel and aluminum-stainless steel clads is challenging, and explosive welding is one of the most suitable processes to achieve them. The present work aims to investigate the coupled e_ect of two strategies for optimizing the production of these clads by explosive welding: the use of a low-density interlayer and the use of a low-density and low-detonation velocity explosive mixture. A broad range of techniques was used to characterize the microstructural and the mechanical properties of the welds, specifically, optical microscopy, scanning electron microscopy, energy dispersive spectroscopy, electron backscatter di_raction, microhardness and tensile-shear testing with digital image correlation analysis. Although aluminum-carbon steel and aluminum-stainless steel have di_erent weldabilities, clads with sound microstructure and good mechanical behavior were achieved for both combinations. These results were associated with the low values of collision point and impact velocities provided by the tested explosive mixture, which made the weldability di_erence between these combinations less significant. The successful testing of this explosive mixture indicates that it is suitable to be used for welding very thin flyers and/or dissimilar materials that easily form intermetallic phases.