- Explosive welding of aluminium to stainless steel using carbon steel and niobium interlayersPublication . Carvalho, Gustavo; Galvão, Ivan; Mendes, R.; Leal, R. M.; Loureiro, AltinoThis work aimed to study aluminium to stainless steel explosive welds produced using two different interlayers: carbon steel and niobium. The use of each interlayer was analysed and compared microstructurally and mechanically using many characterisation techniques. The final joints using both interlayers presented favourable interfacial microstructure: waves on both interfaces. However, the joint using the carbon steel interlayer showed the best mechanical properties compared to the joints using the niobium interlayer. All interfaces found on both welds were wavy. However, depending on the metallic alloy combination, the shape of the wave is completely different. The results suggest that the shape of the waves is influenced by the shock impedance mismatch of the materials being welded. The impedance mismatch parameter (IMP) developed for explosive welding in this work proved to be a compelling method to order metallic combinations in a single axis to estimate the tendency to form typical or curled waves. Typical symmetrical waves tend to develop less quantity of IMCs than curled waves. However, the mechanical tests performed did not detect differences that could have been caused by this difference.
- Explosive welding of aluminium to stainless steelPublication . Carvalho, Gustavo; Galvão, Ivan; Mendes, R.; Leal, Rui; Loureiro, A.Explosive welds of stainless steel and aluminium could only be achieved with the steel positioned as the baseplate. Using stainless steel as the flyer plate, the tensile stresses arrive at the interface before the complete solidification of the localised melting and no bonding is achieved. The poor weldability in this configuration is mainly related to the very low thermal conductivity of the flyer compared to the baseplate. The position of the materials significantly influences the weldability, and the ideal material for the flyer should have a higher melting temperature, specific heat and thermal conductivity, and a lower density compared to the baseplate. Some intermetallic formation is inevitable in dissimilar welds of combinations that can easily form intermetallic phases. The time-velocity diagram proved to be a reliable tool to analyse the weldability, especially when used in conjunction with the weldability window.