Loading...
3 results
Search Results
Now showing 1 - 3 of 3
- Fatigue life of a railway wheel under uniaxial and multiaxial loadingsPublication . Soares, Henrique; Anes, Vitor; de Freitas, M.; Reis, LuisIn this paper, a railway wheel material is under evaluation using multiaxial fatigue testing. The experiments were conducted using a servo-hydraulic machine with standardized specimens. All samples were machined from a single worn-out railway wheel. The damage scale between normal and shear stresses was evaluated in the normal stress space for proportional and non-promotional loadings. Moreover, the uniaxial SN curves were obtained. A critical plane analysis was performed using theoretical criteria and experimental results. Results show a strong influence of heat treatments on the material fatigue behavior.
- Effect of shear/axial stress ratio on multiaxial non-proportional loading fatigue damage on AISI 303 steelPublication . Anes, Vitor; Reis, Luis; de Freitas, M.In this paper, we investigate the cyclic response of AISI 303 stainless steel subjected to non-proportional loads with different amplitude ratios between shear stresses and normal stresses. Based on the experiments, a relationship between the proportional reference load and a varied range of non-proportional loads was established. To achieve this objective, an experimental program was implemented to evaluate the non-proportional parameter Y. Then, the evolution of this parameter was analyzed with the number of cycles to failure and with the ratio between shear and normal stresses, finally, the evolution of the non-proportional parameter Y was mapped by two functions. The results show that the non-proportional response of the AISI 303 can be estimated using the two functions obtained. This allows the estimation of the relationship between non-proportional and proportional stresses as a function of the number of cycles to failure together with the relationship between shear and normal stresses. The results obtained have direct application in the evaluation of accumulated damage, assessed in real-time, resulting from variable amplitude loading spectra. This is of particular interest for the evaluation of structural health monitoring of structures and mechanical components.
- Damage evaluation under complex fatigue loading conditionsPublication . Reis, Luis; Caxias, J.; Soares, Henrique; Rodrigues da Costa, Pedro; Anes, Vitor; Freitas, M.Fatigue damage and life assessment of multiaxial loadings is still an issue yet to resolve. Many methods have been proposed with promising agreements with the experimental results. However, the performance of such methods is, more than often, purely based on fatigue tests with simple loading conditions. In this work the stress scale factor (SSF) criterion and the virtual cycle counting (vcc) method are used to estimate fatigue life and damage accumulation with two damage accumulation rules. Fatigue tests were carried out with three different variable amplitude random loadings, applied to several specimens made from a 42CrMo4 high-strength steel. Fatigue crack plane measurements were compared with predictions from several critical plane models. The applied methods provided very acceptable results making the SSF package (SSF equivalent stress and virtual cycle counting method) a good method to estimate fatigue life and assessment of the damage accumulation in random fatigue loadings.