Loading...
2 results
Search Results
Now showing 1 - 2 of 2
- Simple solvent-free preparation of dispersed composites and their application as catalysts in oxidation and hydrocarboxylation of cyclohexanePublication . Alegria, Elisabete; Fontolan, Emmanuele; Da Costa Ribeiro, Ana Paula; Kopylovich, Maximilian; Domingos, Catarina; Ferraria, Ana Maria; Bertani, Roberta; Botelho do Rego, Ana M.; Pombeiro, ArmandoA simple and clean mechanochemical synthesis at room temperature was employed to prepare CuO-Fe2O3-CoCl2 (100 nm scale), MoO3-V2O5, CuO-CoCl2, Fe2O3-CoCl2, CuO-V2O5, Cu(CH3COO)(2)-V2O5, Cu(CH3COO)(2)-MoO3 (1-100 mm scale) 3d metal based dispersed composites with different ratios of components using simple metal salts/oxides and multiwalled carbon nanotubes (CNT) or graphene oxide (GO) additives (CoCl2-CNT, CoCl2-GO). The thus prepared composite materials were characterized by Xray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), field emission gun scanning electron microscopy (FEGSEM), energy-dispersive X-ray spectroscopy (EDX) and transmission electron microscopy (TEM). XPS analysis revealed no metal redox change upon ball milling treatment, which however promotes metal hydroxylation. The catalytic activity of the prepared composites in the heterogeneous low power microwave-assisted oxidation of cyclohexane with aq. H2O2 at 30 degrees C was notorious with yields up to 31% and selectivity up to 94% towards cyclohexanol (upon treatment with PPh3) for the CuO-CoCl2-based material. The hydro-carboxylation of cyclohexane with CO, water and K2S2O8 to produce cyclohexanecarboxylic acid bearing one more carbon atom at 60 degrees C is achieved with yields up to 17% for the reaction performed in the presence of the CuO-CoCl2 catalyst. The clean CuO-CoCl2 (1:2) catalyst preparation and the catalytic reaction (oxidation of cyclohexane) can be achieved in one-pot at low temperature, without any added organic solvent, and by using exclusively the mechanochemical energy input, with a marked 23% yield at 30 degrees C.
- Comparison of microwave and mechanochemical energy inputs in the catalytic oxidation of cyclohexanePublication . Da Costa Ribeiro, Ana Paula; Alegria, Elisabete; Kopylovich, Maximilian; Ferraria, Ana Maria; Rego, Ana; Pombeiro, ArmandoThe effect of microwave and mechanochemical ball milling energy inputs was studied for the peroxidative oxidation (with aqueous H2O2) of cyclohexane to cyclohexanol and cyclohexanone, over CoCl2 and/or V2O5 dispersed (μm scale) catalysts. A maximum total yield of cyclohexanol and cyclohexanone of 43% after 1 h of reaction at 30 °C, in acetonitrile and under microwave irradiation (5 W), was achieved over the CoCl2–V2O5 (3 : 1) catalyst prepared by ball milling. Cyclohexanol is the main final product with a selectivity of up to 93% over cyclohexanone. Conducting the oxidation reaction under microwave irradiation under the same conditions but without any mechanochemical treatment of the catalyst prior to use resulted in a lower total yield of 30% with a lower selectivity (69%) towards cyclohexanol over cyclohexanone. The sole application of mechanochemical treatment for the catalyst preparation and the catalytic oxidation of cyclohexane allowed to reach yields of 29% after 1 h of reaction, at room temperature, without microwave irradiation and any additive and in the absence of any organic solvent. Ball milling is shown to provide a convenient, solvent-free method to disperse these solid catalysts and to promote the above cyclohexane oxidation, although, in the latter case, not so effectively as microwave irradiation.