Título: Electrodeposition and characterization of nikel-copper metallic foams for application as electrodes for supercapacitors
Autor: Eugénio, S.
Silva, Maria Teresa Oliveira de Moura e
Carmezim, M. J.
Duarte, R. G.
Montemor, M. F.
Palavras-chave: Nickel-Copper
Nanostructured Foams
Electrodeposition
Electrodes for Supercapacitors
Data: Abr-2014
Editora: Springer Netherlands
Citação: EUGÉNIO, S.; [et al] – Electrodeposition and characterization of nikel-copper metallic foams for application as electrodes for supercapacitors. Journal of Applied Electrochemistry. ISSN: 0021-891X. Vol. 44, nr. 4 (2014), pp. 455-465
Resumo: Nickel-copper metallic foams were electrodeposited from an acidic electrolyte, using hydrogen bubble evolution as a dynamic template. Their morphology and chemical composition was studied by scanning electron microscopy and related to the deposition parameters (applied current density and deposition time). For high currents densities (above 1 A cm(-2)) the nickel-copper deposits have a three-dimensional foam-like morphology with randomly distributed nearly-circular pores whose walls present an open dendritic structure. The nickel-copper foams are crystalline and composed of pure nickel and a copper-rich phase containing nickel in solid solution. The electrochemical behaviour of the material was studied by cyclic voltammetry and chronopotentiometry (charge-discharge curves) aiming at its application as a positive electrode for supercapacitors. Cyclic voltammograms showed that the Ni-Cu foams have a pseudocapacitive behaviour. The specific capacitance was calculated from charge-discharge data and the best value (105 F g(-1) at 1 mA cm(-2)) was obtained for nickel-copper foams deposited at 1.8 A cm(-2) for 180 s. Cycling stability of these foams was also assessed and they present a 90 % capacitance retention after 10,000 cycles at 10 mA cm(-2).
Peer review: yes
URI: http://hdl.handle.net/10400.21/4904
DOI: 10.1007/s10800-013-0646-y
ISSN: 0021-891X
1572-8838
Aparece nas colecções:ISEL - Eng. Mecan. - Artigos

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
Eletrodeposition and characterization of nickel.pdf2,62 MBAdobe PDFVer/Abrir    Acesso Restrito. Solicitar cópia ao autor!


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.