Título: Low-Carbon Cement with Waste Oil-Cracking Catalyst Incorporation
Autor: Costa, Carla
Marques, Paulo
Palavras-chave: Blended cements
Cement industry
Low carbon cement
Pozzolanic material
Sustainability
Waste materials
Waste oil-cracking catalyst
Pozzolanic activity
Compressive strenght
Residue FC3R
Spent catalyst
Fluidized-bed
FCC catalyst
Mortars
Corrosion
Pastes
Data: 2012
Editora: IEEE
Citação: Costa C, Marques P. Low-Carbon Cement with Waste Oil-Cracking Catalyst Incorporation. 2012 IEEE-IAS/PCA 54th Cement Industry Technical Conference. 2012.
Resumo: The present paper shows preliminary results of an ongoing project which one of the goals is to investigate the viability of using waste FCC catalyst (wFCC), originated from Portuguese oil refinery, to produce low carbon blended cements. For this purpose, four blended cements were produced by substituting cement CEM I 42.5R up to 20% (w/w) by waste FCC catalyst. Initial and final setting times, consistency of standard paste, soundness and compressive strengths after 2, 7 and 28 days were measured. It was observed that the wFCC blended cements developed similar strength, at 28 days, compared to the reference cement, CEM I 42.5R. Moreover, cements with waste FCC catalyst incorporation up to 15% w/w meet European Standard EN 197-1 specifications for CEM II/A type cement, in the 42.5R strength class.
Peer review: yes
URI: http://hdl.handle.net/10400.21/1836
ISBN: 978-1-4673-0284-5
ISSN: 2155-9139
Aparece nas colecções:ISEL - Eng. Civil - Artigos

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
LOW.rep.pdf267,24 kBAdobe PDFVer/Abrir


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.